Wire Material | SS |
Thickness | 1.2 mm |
Brand | D&H Secheron |
Usage/Application | Autotherme 316L is a solid wire for MIG welding, available in bright finish, gives smooth flow. |
Quantity Per Roll | 15 kg |
Autotherme 316L is a solid wire for MIG welding, available in bright finish, gives smooth flow, stable arc and spatter free under optimum welding conditions. It gives radiographic quality weld deposit. The weld metal has excellent resistance to intergranular corrosion even at elevated temperatures. It is ideally suited for welding stainless steel of similar composition in wrought or cast form and for overlay application to resist heat and corrosion. It is suitable for number of industries like rayon, dye, paper, chemical, fertilizer, petrochemicals, etc.
ApprovalsCHEMICAL COMPOSITION OF SOLID WIRE, WT. %:
Element |
C | Mn | Si | S | P | Cr | Ni | Mo |
Percent |
0.020 | 1.50 | 0.50 | 0.010 | 0.020 | 19.0 | 12.5 | 2.5 |
MECHANICAL PROPERTIES OF ALL WELD METAL
UTS | Elongation |
(MPa) |
(L= 5d)% |
520 | 32.0 |
STANDARD SIZE : Diameter 0.8 mm,1.2 mm & 1.6 mm.
QUANTITY : 12.5 kgs wire, layer wound in a plastic spool that conforms to DIN-8559 SD-300
SHIELDING GAS
Argon
WELDING POSITION
H, F, VU, OH
CURRENT CONDITIONS
DCEP
Wire Material | MS |
Thickness | 1.2 mm |
Brand | D&H Secheron |
Usage/Application | Autotherme Cr-Mo 91 is copper-coated a solid wire for GMAW, yielding 9%Cr - 1%Mo. |
I Deal In | New Only |
Quantity Per Roll | 15 kg |
Autotherme Cr-Mo 91 is copper-coated a solid wire for GMAW, yielding 9%Cr - 1%Mo and modified with Niobium, Vanadium and Nitrogen designed to provide improved creep strength, toughness, fatigue life, oxidation and corrosion resistance at elevated temperatures. The wire gives stable arc, smooth welding performance and deposits radiographic quality welds. It is designed to weld the materials in power plant, refineries, naptha cracker units, etc. Following are some of the steels that can be welded with this wire.
I) Plate: A 387 Gr.91 (II) Pipes: A 335-P91 (III) Tubes: A 213 - T91
ApprovalsCECHEMICAL COMPOSITION OF SOLID WIRE, WT. %:
Element |
C | Mn | Si | P | S | Cr | Ni | Mo | V | Nb | N | Al | Cu |
Percent |
0.11 | 0.95 | 0.25 | 0.007 |
0.008 | 9.35 | 0.35 | 1.0 | 0.2 | 0.03 | 0.04 | 0.02 | 0.10 |
MECHANICAL PROPERTIES OF ALL WELD METAL
(PWHT: 760 C FOR 2 HRS)
UTS | Ys | Elongation |
(MPa) |
(MPa) |
(L= 5d)% |
680 | 550 | 21 |
STANDARD SIZE : 1.2 mm & 1.6 mm.
QUANTITY : 15.0 kg wire, layer wound in a plastic spool that conforms to DIN-8559 SD-300
WELDING PARAMETER : DC(+)
Diameter |
Flat |
|
Volt, V |
Current, A |
|
1.20 mm |
27-32 |
300-360 |
1.60 mm |
25-30 |
340-420 |
SHIELDING GAS
Argon/ 5% CO2
WELDING POSITION
H, F, VU, OH
Wire Material | SS |
Thickness | 1.2 mm |
Brand | D&H SECHERON |
Usage/Application | Autotherme-1414 is a solid wire for MIG welding, available in bright finish, gives smooth flow. |
I Deal In | New Only |
Quantity Per Roll | 12.5 kg |
Autotherme-1414 is a solid wire for MIG welding, available in bright finish, gives smooth flow, stable arc and spatter free under optimum welding conditions. It gives radiographic quality weld deposit. It is used in severe corrosion applications where resistance to reducing, oxidizing, crevice and pitting conditions is required. It is suitable for welding wrought and cast forms of nickel alloys like ASTM B574, B575, B619, B622, and B628 having UNS number N06686 to itself, to steel, to other nickel-base alloys, and for cladding steel.
ApprovalsTYPICAL CHEMICAL COMPOSITION OF SOLID WIRE
Element |
C | Mn | Si | P |
S | Ni | Cr | Mo | W |
Fe | AI | Ti | Cu |
Percent |
0.007 | 0.70 | 0.05 | 0.012 | 0.012 | Rem | 21.5 | 16.0 | 3.8 |
3.0 |
0.20 |
0.10 |
0.30 |
TYPICAL MECHANICAL PROPERTIES OF ALL WELD METAL
UTS | Elongation |
(MPa) |
(L=4d) % |
760 | 35.0 |
STANDARD SIZE: Diameter 0.8 mm, 1.2 mm & 1.6 mm
QUANTITY: 12.5 kgs wire, layer wound in a plastic spool that conforms to DIN 8559 SD-300.
SHIELDING GASArgon
CURRENT CONDITIONSDCEP
WELDING POSITIONSH, F, VU, OH