D&H WELDING CONSUMABLES
Length | 350 mm |
Size/Diameter | 4 mm |
Brand | D&H |
Dia | 4 mm |
Material | Stainless Steel |
Operating Current | AC/DC |
D&H 2209(NS) is a non-synthetic electrode depositing duplex stainless steel weld metal. It is ideal for welding duplex stainless steels. The weld metal possesses excellent corrosion resistance in marine & paper environments. Suitable for welding duplex stainless steels having Cr < 25% and other grades like UNS 32205, UNS 31803, etc.
ApprovalsCETYPICAL CHEMICAL COMPOSITION OF ALL WELD METAL
Element |
C | Mn | Si | P | S | Cr | Ni | Mo | N |
Percent |
0.028 | 1.5 | 0.4 | 0.020 | 0.018 | 22.5 | 8.8 | 3.0 | 0.14 |
TYPICAL MECHANICAL PROPERTIES OF ALL WELD METAL
UTS | YS |
Elongation |
CVN Impact (J) |
Hardness |
(MPa) |
(MPa) |
(L= 5d)% |
at Minus 30°C |
(RC) |
723 | 550 | 25 | 70 |
24 |
CURRENT AND PACKING DATA: AC / DC(+)
Size (mm) Dia x Length |
5x350 | 4x350 |
3.15x350 |
2.5x350 |
Current Range (Amps) |
150-180 | 110-140 |
80-110 |
60-80 |
Weight / Carton (kgs) |
2.5 | 2.5 |
2.5 |
2.5 |
CORROSION PROPERTY
Weld metal meets ASTM A262 Practice C, ASTM G-36, ASTM G-48A and NACE TM-01-77 specification at 350 MPa stress level, 16 bar pressure and 90°C temperature requirements in as welded condition.
FERRITE (FN)40-55
BEND TESTSatisfactory with plunger diameter equal to 4 times the thickness of the specimen.
Length | 350 mm |
Size/Diameter | 4 mm |
Brand | D&H |
Dia | 4 mm |
Material | Stainless Steel |
Operating Current | DC |
D&H 446L is a unique electrode depositing a stainless steel weld metal having a nominal composition of 16Cr - 4.5Ni - 3.5Cu - Cb weld metal. The weld metal possesses excellent properties and attains high strength on heat treatment. It is ideally suited for welding martensitic precipitation hardening stainless steels of the type 17-4 PH etc.
ApprovalsCECHEMICAL COMPOSITION OF ALL WELD METAL (%)
Element |
C | Mn | Si | P | S | Cr | Ni | Mo | Cb | Cu |
Percent |
0.045 | 0.50 | 0.40 | 0.025 | 0.025 | 16.5 | 4.75 | 0.30 | 0.25 | 3.50 |
MECHANICAL PROPERTIES OF ALL WELD METAL
(Heated to 1025°C-1050°C, held for one hour, and air cooled to ambient, and then precipitation hardened at 610-630°C, held for four hours and air cooled to ambient.)
UTS | Elongation |
(MPa) |
(L= 5d)% |
950 | 12.0 |
CURRENT AND PACKING DATA: AC / DC(+)
Size (mm) |
5x350 | 4x350 |
3.15x350 |
2.5x350 |
Current Range (Amps) |
150-180 | 110-140 |
80-100 |
60-80 |
Weight / Carton (kgs) |
2.5 | 2.5 |
2.5 |
2.5 |
Length | 350 mm |
Size/Diameter | 4 mm |
Brand | D&H |
Dia | 4 mm |
Material | Stainless Steel |
Operating Current | AC/DC |
The electrode can be used where resistance to pitting corrosive attack and resistance to stress corrosion cracking are required. The major application area includes, oil & gas industry, offshore platforms, petrochemical plants, mechanical & structural components demanding high strength together with high corrosion resistance.
ApprovalsCECHEMICAL COMPOSITION OF ALL WELD METAL (%)
Element |
C | Mn | Si | S | P | Cr | Ni | Mo | Cu | N |
Percent |
0.025 | 1.1 | 0.45 | 0.010 | 0.012 | 25.0 | 7.5 | 3.3 | 2.0 | 0.17 |
MECHANICAL PROPERTIES OF ALL WELD METAL
UTS | Elongation |
(MPa) |
(L= 5d)% |
782 | 25.0 |
CURRENT AND PACKING DATA: AC / DC(+)
Size (mm) |
5x350 | 4x350 |
3.15x350 |
2.5x350 |
Current Range (Amps) |
150-180 | 110-140 |
80-100 |
60-80 |
Weight / Carton (kgs) |
2.5 | 2.5 |
2.5 |
Length | 350 mm |
Size/Diameter | 4 mm |
Brand | D&H |
Dia | 4 mm |
Material | Stainless Steel |
Operating Current | AC/DC |
D&H 444L is a special purpose electrode depositing12Cr - 4.6Ni - 0.5Mo weld metal, which has excellent resistance to corrosion, erosion, pitting and impact. Ideally suited for joining of similar composition materials, groove welding and surfacing applications. Typical applications include surfacing of high pressure valves, turbine blades, valve seats, repairs of runners, pulp and paper plant equipment, etc.
ApprovalsCECHEMICAL COMPOSITION OF ALL WELD METAL (%)
Element |
C | Mn | Si | Cr | Ni | Mo |
Percent |
0.05 | 0.60 | 0.50 | 12.0 | 4.60 | 0.50 |
MECHANICAL PROPERTIES OF ALL WELD METAL
UTS | Elongation |
Hardness |
(MPa) |
(L= 5d)% |
(VPN) |
782 | 17.0 | 325-360 |
CURRENT AND PACKING DATA: AC / DC(+)
Size (mm) |
5x350 | 4x350 |
3.15x350 |
2.5x350 |
Current Range (Amps) |
150-190 | 110-150 |
80-100 |
60-80 |
Weight / Carton (kgs) |
2.5 | 2.5 |
2.5 |
Length | 350 mm |
Size/Diameter | 4 mm |
Brand | D&H |
Dia | 4 mm |
Material | Stainless Steel |
Operating Current | DC |
D&H 25/4 is stainless steel electrode for high temperature applications. Weld metal has excellent performance in high temperature up to 1100°C and defend against attack of sulphurous oxidizing or reducing combustion gases. Ideally suitable for joining and surfacing on heat-resistant chromium and chromium-nickel steel and cast steel of similar compositions.
ApprovalsTYPICAL CHEMICAL COMPOSITION OF ALL WELD METAL
Element |
C | Mn | Si | S | P | Cr | Ni |
Percent |
0.08 | 1.50 | 0.60 |
0.018 | 0.018 | 25.0 | 5.0 |
TYPICAL MECHANICAL PROPERTIES OF ALL WELD METAL
UTS | YS |
Elongation |
(MPa) |
(MPa) |
(L= 5d)% |
680 |
480 |
18.0 |
CURRENT AND PACKING DATA: DC(+)
Size (mm) Dia x Length |
5x350 | 4x350 |
3.15x350 |
2.5x350 |
Current Range (Amps) |
150-180 | 120-150 |
90-120 |
65-80 |
Weight / Carton (kgs) |
2.5 | 2.5 |
2.5 |
2.5 |
Length | 350 mm |
Size/Diameter | 4 mm |
Brand | D&H |
Dia | 4 mm |
Material | Stainless Steel |
Operating Current | AC/DC |
Rutox-D is a stainless steel electrode depositing an extra low carbon 18Cr - 12Ni - 2.3Mo stainless steel weld metal. The weld metal has excellent resistance to intergranular corrosion even at elevated temperatures. Ideally suited for welding stainless steels of similar composition.
ApprovalsCEEILPDILBHELNTPCCIB-MPNPCILL&T PowerCHEMICAL COMPOSITION OF ALL WELD METAL (%)
Element |
C | Mn | Si | Cr | Ni | Mo | S | P |
Percent |
0.035 | 1.75 | 0.45 | 18.5 | 12.5 | 2.6 | 0.020 | 0.020 |
MECHANICAL PROPERTIES OF ALL WELD METAL
UTS | Elongation |
(MPa) |
(L= 5d)% |
535 | 38.0 |
CURRENT AND PACKING DATA: AC / DC(+)
Size (mm) |
5x350 | 4x350 |
3.15x350 |
2.5x350 |
Current Range (Amps) |
150-180 | 110-140 |
80-100 |
60-80 |
Weight / Carton (kgs) |
2.5 | 2.5 |
2.5 |
2.5 |
Length | 350 mm |
Size/Diameter | 4 mm |
Brand | D&H |
Dia | 4 mm |
Material | Stainless Steel |
Operating Current | AC/DC |
Element |
C | Mn | Si | Cr | Ni | Mo | S | P |
Percent |
0.035 | 0.80 | 0.80 | 18.2 | 12.1 | 2.2 | 0.018 | 0.020 |
MECHANICAL PROPERTIES OF ALL WELD METAL
UTS | Elongation |
(MPa) |
(L= 5d)% |
530 | 35.0 |
CURRENT AND PACKING DATA: AC / DC(+)
Size (mm) |
5x350 | 4x350 |
3.15x350 |
2.5x350 |
Current Range (Amps) |
150-180 | 110-140 |
80-100 |
60-80 |
Weight / Carton (kgs) |
2.0 | 2.0 |
2.0 |
2.0 |
Length | 350 mm |
Size/Diameter | 4 mm |
Brand | D&H |
Dia | 4 mm |
Material | Stainless Steel |
Operating Current | AC/DC |
D&H 320 (NS) is a rutile type non-synthetic all position electrode depositing 20Cr - 35Ni - 2.5Mo - 3.5Cu - Nb weld metal. The weld metal has excellent resistance to oxidation and scaling at 1200 C continuous service. Quiet and stable arc. Less spatter loss good bead appearance with equal ripples. It is primarily used to weld base metals of similar composition for applications where resistance to severe corrosion is required for a wide range of chemicals including sulfuric and sulfurous acid and their salts. These electrodes can be used to weld both castings and wrought alloys of similar composition without post weld heat treatment. The typical applications include HV-9A stainless steel, for fabricating carpenter 20 stainless steels etc.
ApprovalsCETYPICAL CHEMICAL COMPOSITION OF ALL WELD METAL
Element |
C | Mn | Si | S | P | Cr | Ni | Mo | Cu | Nb+Ta |
Percent |
0.05 | 1.20 | 0.40 | 0.020 | 0.020 | 20.5 | 35.0 | 2.50 | 3.5 | 0.55 |
TYPICAL MECHANICAL PROPERTIES OF ALL WELD METAL
UTS | Elongation |
(MPa) |
(L= 5d)% |
590 | 33.0 |
CURRENT AND PACKING DATA: AC / DC(+)
Size (mm) Dia x Length |
5x350 | 4x350 |
3.15x350 |
2.5x350 |
Current Range (Amps) |
150-180 | 110-140 |
80-100 |
60-80 |
Weight / Carton (kgs) |
2.5 | 2.5 |
2.5 |
Size/Diameter | 4 mm |
Brand | D&H |
Dia | 4 mm |
Material | Stainless Steel |
Operating Current | AC/DC |
D&H 309Cb is a stainless steel electrode depositing a 25Cr - 12Ni Niobium stabilised weld metal. Ideally suited for welding stabilised and unstabilised steels to mild steels, welding the clad side of 18-8 or 18-8-Nb clad steels, overlays on ferritic steels, etc.
ApprovalsAdani InfraBHELCETYPICAL CHEMICAL COMPOSITION OF ALL WELD METAL
Element |
C | Mn | Si | Cr | Ni | Nb | S | P |
Percent |
0.07 | 1.50 | 0.50 | 23.50 | 13.00 | 0.80 | 0.020 | 0.025 |
TYPICAL MECHANICAL PROPERTIES OF ALL WELD METAL
UTS | Elongation |
(MPa) |
(L= 5d)% |
624 | 33.0 |
CURRENT AND PACKING DATA: AC / DC(+)
Size (mm) Dia x Length |
5x350 | 4x350 |
3.15x350 |
2.5x350 |
Current Range (Amps) |
140-180 | 110-140 |
80-100 |
60-80 |
Weight / Carton (kgs) |
2.5 | 2.5 |
2.5 |
2.5 |
Length | 350 mm |
Size/Diameter | 4 mm |
Brand | D&H |
Dia | 4 mm |
Material | Stainless Steel |
It is a rutile coated electrode yielding an extra low carbon (0.025% max) with ferrite (6 -12 FN) in the weld metal. The weld metal has excellent resistance to intergranular corrosion even at elevated temperatures.
Element |
C | Mn | Si | S | P | Cr | Ni | Mo |
Percent |
0.021 | 1.75 | 0.30 | 0.020 | 0.022 | 19.0 | 12.0 | 2.4 |
MECHANICAL PROPERTIES OF ALL WELD METAL
UTS | Elongation |
(MPa) |
(L= 4d)% |
535 | 38.0 |
CURRENT AND PACKING DATA: AC / DC(+)
Size (mm) |
5x350 | 4x350 |
3.15x350 |
2.5x350 |
Current Range (Amps) |
150-180 | 110-140 |
80-100 |
60-80 |
Weight / Carton (kgs) |
2.5 | 2.5 |
2.5 |
Length | 350 mm |
Size/Diameter | 4 mm |
Brand | D&H |
Dia | 4 mm |
Material | Stainless Steel |
Operating Current | AC/DC |
D&H 320LR (NS) is a non-synthetic all position electrode depositing 20Cr - 35Ni - 2.5Mo - 3.5Cu - Nb weld metal. The elements C, Si, P and S maintained as low as possible and Nb & Mn are controlled to get better properties. The weld metal has excellent resistance to o oxidation and scaling at 1200°C continuous service. Quiet and stable arc. Less spatter loss good bead appearance with equal ripples. The control on chemistry reduces the weld metal fissuring frequently encountered in fully austenitic stainless steel.
It is primarily used to weld base metals of similar composition for applications where resistance to severe corrosion is required for a wide range of chemicals including sulfuric and sulfurous acid and their salts. These electrodes can be used to weld both castings and wrought alloys of similar composition without post weld heat treatment. The typical applications include HV-9A stainless steel, for fabricating carpenter 20 stainless steels etc.
ApprovalsCETYPICAL CHEMICAL COMPOSITION OF ALL WELD METAL:
Element |
C | Mn | Si | S | P | Cr | Ni | Mo | Cu | Nb+Ta |
Percent |
0.020 | 1.60 | 0.25 | 0.011 | 0.013 | 20.5 | 34.0 | 2.50 | 3.5 | 0.35 |
TYPICAL MECHANICAL PROPERTIES OF ALL WELD METAL
UTS | Elongation |
(MPa) |
(L= 5d)% |
590.0 | 37 |
CURRENT AND PACKING DATA: AC / DC(+)
Size (mm) Dia x Length |
5x350 | 4x350 |
3.15x350 |
2.5x350 |
Current Range (Amps) |
150-180 | 110-140 |
80-100 |
60-80 |
Weight / Carton (kgs) |
2.5 | 2.5 |
2.5 |
2.5 |
Length | 350 mm |
Size/Diameter | 4 mm |
Brand | D&H |
Dia | 4 mm |
Material | Stainless Steel |
Operating Current | AC/DC |
Secheron 33/31 is a rutile coated electrode, depositing 31Ni - 33Cr - 1.6Mo with Nitrogen and low carbon stainless steel weld metal. This electrode is ideally suited for welding Nickel-Chromium-Iron alloy UNS R20033 to itself, and to weld to carbon steel. It is also suitable for welding ASTM B625, B649, B366, B472, B564, B619, B622, and B626 alloys . The electrodes are generally used in the flat position.
ApprovalsTYPICAL CHEMICAL COMPOSITION OF ALL WELD METAL:
Element |
C | Mn | Si | S | P | Cr | Ni | Mo | Cu | N |
Percent |
0.025 | 3.0 | 0.50 | 0.008 | 0.015 | 33.0 | 31.0 | 1.6 | 0.60 | 0.40 |
TYPICAL MECHANICAL PROPERTIES OF ALL WELD METAL:
UTS | Elongation |
(MPa) |
(L= 4d)% |
780 | 32.0 |
CURRENT & PACKING DATA: AC/DC (+)
Size (mm) |
5x350 | 4x350 |
3.15x350 |
2.5x350 |
Current Range (Amps) |
180-220 | 140-180 |
100-140 | 80-100 |
Quantity (kgs/Carton) |
2.5 |
2.5 |
2.5 |
2.5 |
Length | 350 mm |
Size/Diameter | 4 mm |
Brand | D&H |
Dia | 4 mm |
Material | Stainless Steel |
Operating Current | AC/DC |
Rutox-G is a special purpose stainless steel electrode. It is most often used to weld AISI Type 240 and 241 base metals. These alloys are nitrogen-strengthened austenitic stainless steels exhibiting high strength with good toughness over a wide range of temperatures. Significant improvement in resistance to wear in particle-to- metal and metal-to-metal (galling) applications. Nitrogen alloying reduces the tendency for intergranular carbide precipitation in the weld area by inhibiting carbon diffusion and thereby increasing resistance to intergranular corrosion. Nitrogen alloying also improves resistance to pitting and crevice corrosion in aqueous chloride containing media. It exhibit improved resistance to trans granular stress corrosion cracking in hot aqueous chloride containing media. It is also suitable for welding dissimilar steels like mild steel and stainless steels, and also suitable for overlay on mild steel for corrosion and wear applications.
ApprovalsTYPICAL CHEMICAL COMPOSITION OF ALL WELD METAL
Element |
C | Mn | Si | S | P | Cr | Ni | N |
Percent |
0.04 | 12.0 | 0.70 | 0.020 | 0.033 | 18.0 |
5.0 | 0.15 |
TYPICAL MECHANICAL PROPERTIES OF ALL WELD METAL
UTS | Elongation |
(MPa) |
(L= 4d)% |
720 | 18.0 |
CURRENT AND PACKING DATA : AC / DC(+)
Size (mm) Dia x Length |
5x350 | 4x350 |
3.15x350 |
2.5x350 |
Current Range (Amps) |
160-200 | 130-160 |
90-120 |
60-100 |
Weight / Carton (kgs) |
2.5 | 2.5 |
2.5 |
2.5 |
Length | 350 mm |
Size/Diameter | 3 mm |
Brand | D&H |
Dia | 3.15 mm |
Material | Stainless Steel |
Application/Usage | Automotive, Manufacturing, Construction, Fabrication |
Packaging Type | Box |
Certification | AWS ISO |
Country of origin | Made in India |
Grade | 6013 |
Size/Diameter | 3 mm |
Length | 350 mm |
Brand | D&H |
Material | Mild Steel |
Pieces per pack | 85x6 |
Operating Current | AC/DC |
Application/Usage | Automotive, Construction, Fabrication, Manufacturing |
Packaging Type | Box |
Certification | ISI |
Country of origin | Made in India |
A medium coated general purpose all position electrode for welding low carbon and mild structural steels. It gives radiographic quality weld metal. The electrode operates with a quiet arc and deposits a smooth bead with fine ripples. The slag is easily detachable. The electrode produces minimum spatter and has good striking and re-striking characteristics. The electrode operates well under low OCV transformers and direct current either polarity. Easy to operate in all positions including vertical down. Typical applications include welding of steel structures, tanks, truck frames and bodies, machinery construction, auto bodies, frames, pipes etc.
Grade | 6013 |
Size/Diameter | 4 mm |
Length | 450 mm |
Brand | D&H |
Material | Mild Steel |
Pieces per pack | 55x6 |
Operating Current | AC/DC |
Application/Usage | Manufacturing, Fabrication, Automotive, Construction |
Packaging Type | Box |
Certification | ISI |
Country of origin | Made in India |
A medium coated general purpose all position electrode for welding low carbon and mild structural steels. It gives radiographic quality weld metal. The electrode operates with a quiet arc and deposits a smooth bead with fine ripples. The slag is easily detachable. The electrode produces minimum spatter and has good striking and re-striking characteristics. The electrode operates well under low OCV transformers and direct current either polarity. Easy to operate in all positions including vertical down. Typical applications include welding of steel structures, tanks, truck frames and bodies, machinery construction, auto bodies, frames, pipes etc.
Grade | 6013 |
Size/Diameter | 2 mm |
Length | 350 mm |
Brand | D&H |
Material | Mild Steel |
Operating Current | AC/DC |
Application/Usage | Automotive, Fabrication, Manufacturing, Construction |
Packaging Type | Box |
Certification | ISI |
Country of origin | Made in India |
A medium coated general purpose all position electrode for welding low carbon and mild structural steels. It gives radiographic quality weld metal. The electrode operates with a quiet arc and deposits a smooth bead with fine ripples. The slag is easily detachable. The electrode produces minimum spatter and has good striking and re-striking characteristics. The electrode operates well under low OCV transformers and direct current either polarity. Easy to operate in all positions including vertical down. Typical applications include welding of steel structures, tanks, truck frames and bodies, machinery construction, auto bodies, frames, pipes etc.
Grade | 6013 |
Size/Diameter | 5 mm |
Length | 450 mm |
Brand | D&H |
Material | Mild Steel |
Pieces per pack | 35x6 |
Operating Current | AC/DC |
Application/Usage | Fabrication, Automotive, Manufacturing, Construction |
Packaging Type | Box |
Certification | ISI |
Country of origin | Made in India |
A medium coated general purpose all position electrode for welding low carbon and mild structural steels. It gives radiographic quality weld metal. The electrode operates with a quiet arc and deposits a smooth bead with fine ripples. The slag is easily detachable. The electrode produces minimum spatter and has good striking and re-striking characteristics. The electrode operates well under low OCV transformers and direct current either polarity. Easy to operate in all positions including vertical down. Typical applications include welding of steel structures, tanks, truck frames and bodies, machinery construction, auto bodies, frames, pipes etc.