Minimum Order Quantity | 12 Kg |
Wire Material | 1.2 mm |
Autotherme-1250 is a solid wire for GMAW welding, available in bright finish, gives smooth flow, stable arc and spatter free under optimum welding conditions. It gives radiographic quality welds. The weld metal possesses good resistance to corrosion by sea water, chlorinated solvents, sulfuric acid and alkalies. It is ideally suited for welding of monel to monel, Ni-Cu alloys to themselves, Ni-Cu alloy to steels, for welding clad side of Ni-Cu clad steel and for surfacing on steel parts. It is ideal for marine, chemical, food, dairy and oil refining industries.
ApprovalsCHEMICAL COMPOSITION OF ALL WELD METAL (%)
Element |
C | Mn | Si | S | P | Ni | Cu | Ti |
Percent |
0.025 | 0.87 | 0.16 | 0.006 | 0.010 | 63.80 | 31.0 | 2.50 |
TYPICAL MECHANICAL PROPERTIES OF ALL WELD METAL
UTS | Elongation |
(MPa) |
(L= 4d)% |
520 | 30.0 |
Argon
CURRENT CONDITIONSDCEP
WELDING POSITIONSH, F, VU, OH
PACKINGSTANDARD SIZE: Diameter 0.8 mm, 1.2 mm & 1.6 mm
QUANTITY 12.5 kgs wire, layer wound in a plastic spool that conforms to DIN 8559 SD-300.
Minimum Order Quantity | 12 Kg |
Wire Material | 1.2 mm |
Autotherme 1423 is a solid wire for MIG welding, available in bright finish, gives smooth flow, stable arc and spatter free under optimum welding conditions. It gives radiographic quality weld deposit. This is suitable for welding Ni-Cr-Mo alloys as well as the clad side of joints in steel clad with a Ni-Cr-Mo alloy and for welding Ni- Cr-Mo alloys to steel and to other nickel base alloys. It is suitable for welding components in plants for chemical processes with highly corrosive media. Typical base materials which are welded with this product are ASTM B574, B575, B619, B622 and B626 with UNS No. N06022. Ideal for C-22 alloys.
ApprovalsCHEMICAL COMPOSITION OF ALL WELD METAL (%)
Element |
C | Mn | Si | P | S | Cr | Ni | Mo | W | Fe | Cu | V | Co |
Percent |
0.012 | 0.25 | 0.06 | 0.015 | 0.008 | 21.0 | Rem | 13.5 | 3.0 | 4.0 | 0.30 | 0.20 | 0.8 |
TYPICAL MECHANICAL PROPERTIES OF ALL WELD METAL
UTS | Elongation |
(MPa) |
(L= 4d)% |
740 | 35.0 |
Argon
CURRENT CONDITIONSDCEP
WELDING POSITIONSH, F, VU, OH
PACKINGSTANDARD SIZE: Diameter 0.8 mm, 1.2 mm & 1.6 mm
QUANTITY 12.5 kgs wire, layer wound in a plastic spool that conforms to DIN 8559 SD-300.
Minimum Order Quantity | 12 Kg |
Wire Material | 1.2 mm |
AUTOTHERME 309 is a solid wire for MIG welding, available in bright finish, gives smooth flow, stable arc and spatter free under optimum welding conditions. It gives radiographic quality weld deposit. The weld metal has excellent mechanical properties and possesses good oxidation and scaling resistance at elevated temperatures. It is ideally suited for welding stainless steels, wrought and cast materials of similar composition, welding of 18/8 type stainless steels to carbon steels for buffer layers, for welding clad side of 18/8 clad stainless steels, etc.
ApprovalsCHEMICAL COMPOSITION OF SOLID WIRE, WT. %:
Element |
C | Mn | Si | P | S | Cr | Ni |
Percent |
0.05 | 1.75 | 0.35 | 0.018 | 0.015 | 23.3 | 13.8 |
MECHANICAL PROPERTIES OF ALL WELD METAL
UTS | Elongation |
(MPa) |
(L= 4d)% |
570 | 32.0 |
STANDARD SIZE : Diameter 0.8 mm,1.2 mm & 1.6 mm.
QUANTITY : 12.5 kgs wire, layer wound in a plastic spool that conforms to DIN-8559 SD-300
SHIELDING GAS
Argon
WELDING POSITION
H, F, VU, OH
CURRENT CONDITIONS
DCEP
Minimum Order Quantity | 12 Kg |
Wire Material | 1.2 mm |
Autotherme 309LMo is a solid wire for MIG welding, available in bright finish, gives smooth flow, stable arc and spatter free under optimum welding conditions. It gives radiographic quality weld deposit. A highly crack resistant weld deposit which displays good intergranular corrosion resistance and good oxidation and scaling resistance at elevated temperatures. For welding stainless steel of similar composition in wrought or cast form and for overlay application to resist heat and corrosion. Suitable for joining dissimilar steels, such 18-11-Mo steel to mild steel, clad side welding of 18-11-Mo steel, and for buffer layer applications.
ApprovalsCHEMICAL COMPOSITION OF SOLID WIRE, WT. %:
Element |
C | Mn | Si | P | S | Cr | Ni | Mo |
Percent |
0.02 | 1.50 | 0.35 | 0.020 | 0.010 | 24.0 | 13.0 | 2.5 |
MECHANICAL PROPERTIES OF ALL WELD METAL
UTS | Elongation |
(MPa) |
(L= 5d)% |
580 | 32.0 |
STANDARD SIZE : Diameter 0.8 mm,1.2 mm & 1.6 mm.
QUANTITY : 12.5 kgs wire, layer wound in a plastic spool that conforms to DIN-8559 SD-300
SHIELDING GAS
Argon
WELDING POSITION
H, F, VU, OH
CURRENT CONDITIONS
DCEP