Length | 350 mm |
Size/Diameter | 4 mm |
Brand | D&H |
Dia | 4 mm |
Material | Stainless Steel |
Rutox-Mo (St) is a stainless steel electrode producing a Niobium stabilised 18Cr - 12Ni - 2.3Mo weld metal. The weld metal possesses good resistance to corrosion and pitting and improved creep strength. The weld metal has excellent resistance to intergranular corrosion. Ideally suited for joining stainless steels of similar composition.
ApprovalsCEEILCHEMICAL COMPOSITION OF ALL WELD METAL (%)
Element |
C | Mn | Si | Cr | Ni | Mo | Nb | S | P |
Percent |
0.05 | 1.5 | 0.42 | 18.5 | 12.0 | 2.3 | 0.60 | 0.018 | 0.020 |
MECHANICAL PROPERTIES OF ALL WELD METAL
UTS | Elongation |
(MPa) |
(L= 5d)% |
594 | 35.0 |
CURRENT AND PACKING DATA: AC / DC(+)
Size (mm) |
5x350 | 4x350 |
3.15x350 |
2.5x350 |
Current Range (Amps) |
150-180 | 110-140 |
80-100 |
60-80 |
Weight / Carton (kgs) |
2.5 | 2.5 |
2.5 |
Length | 350 mm |
Size/Diameter | 4 mm |
Brand | D&H |
Dia | 4 mm |
Material | Stainless Steel |
Operating Current | AC/DC |
SIA(Rutile) is an electrode depositing 18Cr-8Ni-5Mn weld metal. Ideally suited for joining and surfacing applications to enhance resistance to impact and abrasion. Ideally suited for joining austenitic manganese steel to carbon steel, low alloy steel, etc. , and also for buffer layers on a variety of steels.
ApprovalsCHEMICAL COMPOSITION OF ALL WELD METAL (%)
Element |
C | Mn | Si | Cr | Ni |
Percent |
0.07 | 6.0 | 0.60 | 19.0 | 9.0 |
MECHANICAL PROPERTIES OF ALL WELD METAL
UTS | Elongation |
Hardness |
(MPa) |
(L= 4d)% |
200-220 BHN (As welded) |
614 | 35.0 | 500 BHN (Work hardens under impact) |
CURRENT AND PACKING DATA: AC / DC(+)
Size (mm) |
5x350 | 4x350 |
3.15x350 |
2.5x350 |
Current Range (Amps) |
190-240 | 140-190 |
90-130 |
60-100 |
Qty. (Pcs./Carton) |
25 | 40 | 60 | 80 |
Length | 350 mm |
Size/Diameter | 4 mm |
Brand | D&H |
Dia | 4 mm |
Material | Stainless Steel |
Operating Current | AC/DC |
• Stainless steel electrode for welding of similar and dissimilar steels.
• The weld deposit displays good corrosion, scaling resistance and crack resistance.
• It meets customer requirements economically.
• It works well with transformer having low OCV also.
• It is ideally suited for welding similar alloys in wrought or cast form.
• It can also used for welding dissimilar metals, such as joining SS304L to carbon. steel, welding the clad side of SS304L clad steels, and applying stainless steel sheet lining to carbon steel shells.
ApprovalsCECHEMICAL COMPOSITION OF ALL WELD METAL (%)
Element |
C | Mn | Si | Cr | Ni | S | P |
Percent |
0.035 | 0.80 | 0.80 | 23.0 | 12.5 | 0.022 | 0.025 |
MECHANICAL PROPERTIES OF ALL WELD METAL
UTS | Elongation |
(MPa) |
(L= 5d)% |
550 | 35.0 |
CURRENT AND PACKING DATA: AC / DC(+)
Size (mm) |
5x350 | 4x350 |
3.15x350 |
2.5x350 |
Current Range (Amps) |
150-180 | 110-140 |
80-110 |
60-80 |
Weight / Carton (kgs) |
2.0 | 2.0 |
2.0 |
2.0 |
Length | 350 mm |
Size/Diameter | 4 mm |
Brand | D&H |
Dia | 4 mm |
Material | Stainless Steel |
Operating Current | DC |
Batox-F(U)M is a basic coated electrode depositing fully austenitic stainless steel weld metal. The deposit possesses excellent crack resistance and is suitable for welding for high pressure parts of urea plant equipment to resist severe corrosion. It is ideally suited for welding of stainless steels of similar composition and their equivalents for overlays, surfacing applications, etc.
ApprovalsTYPICAL CHEMICAL COMPOSITION OF ALL WELD METAL
Element |
C | Mn | Si | S | P | Cr | Ni | Mo | N |
Percent |
0.035 | 5.50 | 0.45 | 0.015 | 0.025 | 18.8 | 16.5 | 3.00 | 0.11 |
TYPICAL MECHANICAL PROPERTIES OF ALL WELD METAL
UTS | Elongation |
(MPa) |
(L= 4d)% |
620 | 30 |
CURRENT AND PACKING DATA: AC / DC(+)
Size (mm) |
5x350 | 4x350 |
3.15x350 |
2.5x350 |
Current Range (Amps) |
150-180 | 110-140 |
80-100 |
60-80 |
Weight / Carton (kgs) |
2.5 | 2.5 |
2.5 |
2.5 |
Length | 350 mm |
Size/Diameter | 4 mm |
Brand | D&H |
Dia | 4 mm |
Material | Stainless Steel |
Operating Current | AC/DC |
Rutox-B(SPL) is a rutile coated electrode yielding an extra low carbon (0.028% max) with ferrite (5-10 FN) in the weld metal. The weld metal has excellent resistance to intergranular corrosion even at elevated temperatures.
• Ideally suited for welding stainless steels of similar composition.
• Ideal for joining wrought and cast materials.
• Surfacing & overlay applications.
ApprovalsCHEMICAL COMPOSITION OF ALL WELD METAL (%)
Element |
C | Mn | Si | S | P | Cr | Ni |
Percent |
0.025 | 1.75 | 0.30 | 0.020 | 0.022 | 20.0 | 10.0 |
MECHANICAL PROPERTIES OF ALL WELD METAL
UTS | Elongation |
(MPa) |
(L= 4d)% |
535 | 38.0 |
CORROSION PROPERTY : Weld metal meets ASTM A262 Practice E
CURRENT AND PACKING DATA: AC / DC(+)
Size (mm) |
5x350 | 4x350 |
3.15x350 |
2.5x350 |
Current Range (Amps) |
150-180 | 110-140 |
80-110 |
60-80 |
Weight / Carton (kgs) |
2.5 | 2.5 |
2.5 |
2.5 |
Length | 350 mm |
Size/Diameter | 4 mm |
Brand | D&H |
Dia | 4 mm |
Material | Stainless Steel |
Operating Current | AC/DC |
Rutox-A(N) is a stainless steel electrode depositing 22Cr - 10Ni - 0.15N weld metal. It is a special electrode producing stainless steel weld metal which has excellent operational characteristics. The weld metal has higher resistance to cracking, oxidation and scaling at elevated temperatures up to 1100 C. It is ideally suited for welding of stainless steels of similar composition like ASTM S30815 and equivalent, for overlays, surfacing and repairing castings.
ApprovalsTYPICAL CHEMICAL COMPOSITION OF ALL WELD METAL (%)
Element |
C | Mn | Si | S | P | Cr | Ni | N |
Percent |
0.080 | 0.75 | 0.90 | 0.010 | 0.020 |
22.0 | 10.5 | 0.15 |
TYPICAL MECHANICAL PROPERTIES OF ALL WELD METAL
UTS | Elongation |
CVN Impact Strength |
(MPa) |
(L= 4d)% |
at minus 20°C (Joules) |
680 | 38.0 | 60 |
CURRENT & PACKING DATA: AC / DC (+)
Size (mm) |
5x350 | 4x350 |
3.15x350 |
2.5x350 |
Current Range (Amps) |
150-180 | 110-140 |
80-100 |
60-80 |
Weight / Carton (kgs) |
2.5 | 2.5 |
2.5 |
2.5 |
Length | 350 mm |
Size/Diameter | 4 mm |
Brand | D&H |
Dia | 4 mm |
Material | Stainless Steel |
Operating Current | DC |
Basic coated electrode depositing low carbon 19Cr - 10Ni stainless steel weld metal which has excellent resistance to Intergranular Corrosion. The weld metal has higher resistance to cracking, oxidation, and scaling at elevated temperatures. It is ideally suited for welding of stainless steels of similar composition like 304L and equivalents, for overlays, surfacing, and repairing castings of similar materials.
ApprovalsBHELNPCILCHEMICAL COMPOSITION OF ALL WELD METAL (%)
Element |
C | Mn | Si | P | S | Cr | Ni |
Percent |
0.03 | 1.40 | 0.40 | 0.020 | 0.020 | 19.8 | 10.0 |
UTS | Elongation |
CVN Impact strength |
Lateral Expansion at |
(MPa) |
(L= 4d)% |
at minus 196°C (J) |
at minus 196°C (mm) |
565 | 40.0 | 45 |
0.50 |
CURRENT AND PACKING DATA: DC(+)
Size (mm) |
5x350 | 4x350 |
3.15x350 |
2.5x350 |
Current Range (Amps) |
150-180 | 110-140 |
80-100 |
60-80 |
Quantity (Carton/kgs) |
2.5 | 2.5 |
2.5 |
2.5 |
Length | 350 mm |
Size/Diameter | 4 mm |
Brand | D&H |
Dia | 4 mm |
Material | Stainless Steel |
Operating Current | AC/DC |
SIA-Mo is a special stainless steel electrode depositing a stainless steel weld metal having 19Cr - 9Ni - 6Mn - 0.4Mo. The weld metals highly crack resistant and its unique mechanical properties are maintained even when welding steels of different compositions. It is ideally suited for welding HSLA steels like armour steels etc. in cast or rolled forms. It is also useful for welding materials of similar composition, austenitic manganese steel and for producing stainless steel overlay for corrosion resistance, buffer layers for hard facing and work hardenable deposits.
ApprovalsTYPICAL CHEMICAL COMPOSITION OF ALL WELD METAL (%)
Element |
C | Mn | Si | Cr | Ni | Mo | S | P |
Percent |
0.06 | 6.10 | 0.73 | 19.8 | 8.9 | 0.42 | 0.014 | 0.026 |
TYPICAL MECHANICAL PROPERTIES OF ALL WELD METAL
UTS | Elongation |
(MPa) |
(L= 4d)% |
590 | 38.0 |
CURRENT & PACKING DATA: AC / DC (+)
Size (mm) |
6.0x350 | 5x350 | 4x350 |
3.15x350 |
2.5x350 |
Current Range (Amps) |
220-260 | 160-200 | 120-160 |
80-110 |
60-80 |
Qty. (Pcs./Carton) |
3.0 | 2.5 | 2.5 | 2.5 |
Length | 350 mm |
Size/Diameter | 4 mm |
Brand | D&H |
Dia | 4 mm |
Material | Stainless Steel |
Operating Current | AC/DC |
Rutox-A is a stainless steel electrode yielding a weld metal of 19Cr - 10Ni. The weld metal displays good resistance to cracking, corrosion and scaling. This stainless steel welding rod is ideally suited for welding stainless steel materials of similar composition like AISI 301, 302, 304, 308, etc.
ApprovalsCEEILPDILAdani InfraBHELNTPCNPCILCHEMICAL COMPOSITION OF ALL WELD METAL (%)
Element |
C | Mn | Si | Cr | Ni | S | P |
Percent |
0.05 | 1.40 | 0.40 | 19.5 | 9.50 | 0.020 | 0.020 |
MECHANICAL PROPERTIES OF ALL WELD METAL
UTS | Elongation |
(MPa) |
(L= 5d)% |
604 | 38 |
CURRENT AND PACKING DATA: AC / DC(+)
Size (mm) |
5x350 | 4x350 |
3.15x350 |
2.5x350 |
Current Range (Amps) |
140-180 | 110-140 |
80-100 |
60-80 |
Weight / Carton (kgs) |
2.5 | 2.5 |
2.5 |
2.5 |
Length | 350 mm |
Size/Diameter | 4 mm |
Brand | D&H |
Dia | 4 mm |
Material | Stainless Steel |
Operating Current | AC/DC |
SIA (N) is a low-hydrogen type special stainless steel electrode depositing a stainless steel weld metal having 16Cr 8Ni - 8Mn - 0.4Mo 0.12N. The weld metal highly crack resistant and it has got high strength and good toughness properties even at different temperatures. Nitrogen alloying in this weld metal increases wear resistance and satisfy galling resistant requirements. It is ideally suited for resisting wear in particle to metal & metal-to-metal applications. It is also useful for producing stainless steel overlay for corrosion resistance, surfacing layers for hardfacing and work hardenable deposits.
ApprovalsTYPICAL CHEMICAL COMPOSITION OF ALL WELD METAL (%)
Element |
C | Mn | Si | Cr | Ni | Mo | S | P | N | V | W | Cb | Cu |
Percent |
0.07 | 8.0 | 0.90 | 16.5 |
8.2 |
0.42 |
0.014 |
0.026 | 0.12 | 0.10 | 0.10 |
0.2 | 0.2 |
TYPICAL MECHANICAL PROPERTIES OF ALL WELD METAL
UTS | Elongation |
(MPa) |
(L= 4d)% |
630 | 38.0 |
CURRENT & PACKING DATA: AC / DC (+)
Size (mm) |
6x350 | 5x350 |
4x350 |
3.15x350 |
2.5x350 |
Current Range (Amps) |
220-270 | 170-200 | 130-170 | 90-130 | 60-90 |
Qty. (Pcs./Carton) |
3.0 | 2.5 | 2.5 | 2.5 |
Length | 350 mm |
Size/Diameter | 4 mm |
Brand | D&H |
Dia | 4 mm |
Material | Stainless Steel |
Operating Current | AC/DC |
Rutox-F(U) is a rutile coated electrode depositing a weld metal which is fully austenitic in structure, has high strength and good crack resistance. The weld metal displays remarkable corrosion resistance particularly in urea service. It is ideally suitable for welding of AISI 316L and their nitrogen bearing versions particularly for urea service.
ApprovalsTYPICAL CHEMICAL COMPOSITION OF ALL WELD METAL (%)
Element |
C | Mn | Si | S | P | Cr | Ni | Mo | N |
Percent |
0.030 | 4.0 | 0.45 | 0.015 | 0.025 | 19.5 | 16.0 | 2.8 | 0.14 |
TYPICAL MECHANICAL PROPERTIES OF ALL WELD METAL
UTS | Elongation |
(MPa) |
(L= 4d)% |
630 | 37.0 |
CURRENT & PACKING DATA: AC / DC (+)
Size (mm) |
5x350 | 4x350 |
3.15x350 |
2.5x350 |
Current Range (Amps) |
150-180 | 110-140 |
80-100 |
60-80 |
Weight / Carton (kgs) |
2.5 | 2.5 |
2.5 |
2.5 |
Length | 350 mm |
Size/Diameter | 4 mm |
Brand | D&H |
Dia | 4 mm |
Material | Stainless Steel |
Operating Current | DC |
SIA is a basic coated multipurpose stainless steel electrode producing a weld metal of 18Cr - 9Ni - 5Mn. The weld metal has excellent crack resistance and has good o scaling resistance up to 850 C. Ideal for joining ferritic to austenitic steels, armour plates, austenitic manganese steels, heat resistant steels, dissimilar materials, for buffer layers etc.
ApprovalsCHEMICAL COMPOSITION OF ALL WELD METAL (%)
Element |
C | Mn | Si | S | P | Cr | Ni |
Percent |
0.09 | 5.50 | 0.60 | 0.015 | 0.025 | 19.5 | 9.2 |
MECHANICAL PROPERTIES OF ALL WELD METAL
UTS | Elongation |
(MPa) |
(L= 4d)% |
644 | 38 |
CURRENT AND PACKING DATA: DC (+)
Size (mm) |
5x450 | 4x350 |
3.15x350 |
2.5x350 |
Current Range (Amps) |
170-200 | 130-170 |
90-130 |
60-90 |
Weight/Carton (kgs) |
2.5 | 2.5 |
2.5 |
Length | 350 mm |
Size/Diameter | 4 mm |
Brand | D&H |
Dia | 4 mm |
Material | Stainless Steel |
Operating Current | AC/DC |
Rutox-F(SPL) is a stainless steel electrode depositing zero ferrite weld metal which displays excellent resistance to corrosion particularly in urea service. The welds are of radiographic quality and possess excellent corrosion resistance. Ideally suited for welding AISI 316L and their equivalents for chemical and fertilizer industries.
ApprovalsCHEMICAL COMPOSITION OF ALL WELD METAL (%)
Element |
C | Mn | Si | Cr | Ni | Mo | S | P |
Percent |
0.025 | 2.0 | 0.50 | 17.5 | 15.0 | 2.60 | 0.020 | 0.020 |
MECHANICAL PROPERTIES OF ALL WELD METAL
UTS | Elongation |
CVN Impact strength (J) |
(MPa) |
(L= 5d)% |
at minus 196°C (J) |
574 | 36 | 27 |
CURRENT AND PACKING DATA: AC / DC(+)
Size (mm) |
5x350 | 4x350 |
3.15x350 |
2.5x350 |
Current Range (Amps) |
150-180 | 110-140 |
80-100 |
60-80 |
Weight / Carton (kgs) |
2.5 | 2.5 |
2.5 |
2.5 |