Wire Material | MS |
Thickness | 1.2 mm |
Brand | D&H Secheron |
Usage/Application | Autotherme Cr-Mo 2 (MOD) is a copper-coated solid wire for GMAW, available in bright finish. |
Quantity Per Roll | 12.5 kg, 15 kg |
Autotherme Cr-Mo 2 (MOD) is a copper-coated solid wire for GMAW, available in bright finish, gives smooth flow, stable arc and spatter free under optimum welding conditions. This wire having lesser impurities i.e. S, P, will improve the subzero impact property. It gives radiographic quality welds. It is suitable for welding 2.25Cr - 1Mo steel. The weld metal possesses good high temperature properties. Especially suitable for welding of pipes and tubes of matching composition in Power plants, Refineries, Petrochemicals, Fertilizer plants, etc. Suitable for welding of ASTM steels: Grade F22 (class 1 & 3) of SA-182 and SA-336, Grade T4, T22 of SA- 199, Grade T22 of SA-213, Grade WC9 of SA-217, Grade P22 of SA-335, Grade FP22 of SA-369, Grade 22, 22L of SA-387, Grade CP22 of SA-426, Grade 22 of SA- 541, Class 1 of A, B types of SA-542, etc.
ApprovalsCETYPICAL CHEMICAL COMPOSITION OF SOLID WIRE
Element |
C | Mn | Si | S | P | Cr | Mo | Cu | Sn | As | Sb |
Percent |
0.08 | 0.46 | 0.50 | 0.007 | 0.009 | 2.50 | 1.00 | 0.05 | 0.003 | 0.003 | 0.002 |
X-factor: (10P + 5Sb + 4Sn + As) / 100 ≤ 12 ppm (elements in ppm)
J-factor: (Mn+Si) x (P+Sn) 10 ≤ 120
TYPICAL MECHANICAL PROPERTIES OF ALL WELD METAL(PWHT: 690°C FOR 1 HR)
UTS | Ys | Elongation |
CVN Impact Strength (J) |
(MPa) |
(MPa) |
(L= 5d)% |
At minus 20°C |
680 | 600 | 22 |
50 |
PACKING
STANDARD SIZE : 1.2 mm & 1.6 mm
QUANTITY : 15.0 kg wire, random/ layer wound in a plastic spool that conforms to DIN-8559 SD-300.
WELDING PARAMETER : DC(+)
Diameter |
Flat |
|
Volt, V |
Current, A |
|
1.2 mm |
27-32 |
300-360 |
1.6 mm |
25-30 |
340-420 |
SHIELDING GAS
Argon/ 1-5% O2
WELDING POSITION
H, F, VU, OH
Wire Material | MS |
Thickness | 1.2 mm |
Brand | D&H Secheron |
Usage/Application | Autotherme Mn-Mo is a copper-coated solid wire for GMAW, available in bright finish. |
I Deal In | New Only |
Quantity Per Roll | 15 kg |
Autotherme Mn-Mo is a copper-coated solid wire for GMAW, available in bright finish, gives smooth flow, stable arc and spatter free under optimum welding conditions. It gives radiographic quality welds. It is suitable for welding high strength fine-grained structural steels containing ~0.5%Mo. The wire is also suitable for welding of penstock pipe-line, fabrication of earth moving equipments, etc. where high tensile strength property is desired from the weld metal. Suitable for welding of ASTM steels: SA-455/ SA-455M, Gr.60, Gr.65 steels of SA-515/ SA- 515M, Gr.60, Gr.65 steels of SA-516/ SA-516M, Class 1 of A, B, C, D grades of SA- 533/ SA-533M, etc.
ApprovalsCECHEMICAL COMPOSITION OF SOLID WIRE, WT. %:
Element |
C | Mn | Si | S | P | Mo | Cu |
Percent |
0.06 | 1.75 | 0.53 | 0.010 | 0.015 | 0.40 | 0.15 |
MECHANICAL PROPERTIES OF ALL WELD METAL
UTS | Ys | Elongation |
(MPa) |
(MPa) |
(L= 5d)% |
640 | 540 | 23.0 |
CURRENT AND PACKING DATA:
STANDARD SIZE : 1.2 mm & 1.6 mm
QUANTITY : 15.0 kgs wire, layer wound in a plastic spool that conforms to DIN-8559 SD-300.
WELDING PARAMETER: DC(+)
Diameter |
Flat |
|
Volt, V |
Current, A |
|
1.20 mm |
27-32 |
300-360 |
1.60 mm |
25-30 |
340-420 |
SHIELDING GAS
CO2/ 80% Ar & 20 % CO2
WELDING POSITION
H,F,VU,OH
Wire Material | MS |
Thickness | 1.2 mm |
Brand | D&H Secheron |
Usage/Application | Autotherme Cr-Mo 1 (MOD) is a copper-coated solid wire for GMAW available in bright finish. |
I Deal In | New Only |
Quantity Per Roll | 15 kg |
Autotherme Cr-Mo 1 (MOD) is a copper-coated solid wire for GMAW available in bright finish, gives smooth flow, stable arc and spatter free under optimum welding conditions. This wire having lesser impurities i.e. S, P, will improve the subzero impact property. It gives radiographic quality welds. It is suitable for welding 1.25Cr - 0.5Mo steel. The weld metal possesses good high temperature properties. Especially suitable for welding of pipes & tubes of matching composition in Power plants, Refineries, Petrochemicals, Fertilizer plants, etc. Suitable for welding of ASTM steels: Grade F2, F11, F12 class 1 & 2 of SA-182, Grade T11of SA-199, Grade T2, T11 & T12 of SA-213, Grade WC6 of SA-217, Grade P2, P11 & P12 of SA-335, Grade FP2, FP11 & FP12 of SA-369, Grade 2, 11 & 12 of SA-387, Grade CP2, CP11 & CP12 of SA-426, etc.
ApprovalsCECHEMICAL COMPOSITION OF SOLID WIRE, WT. %:
Element |
C | Mn | Si | S | P | Cr | Mo | Cu | Sn | As | Sb |
Percent |
0.08 | 0.50 | 0.45 | 0.007 | 0.009 | 1.30 | 0.50 | 0.05 | 0.003 | 0.003 | 0.002 |
X-factor: (10P + 5Sb + 4Sn + As) / 100 ≤ 12 ppm (elements in ppm)
J-factor: (Mn+Si) x (P+Sn) 10 ≤ 120
MECHANICAL PROPERTIES OF ALL WELD METAL
UTS | Ys | Elongation |
CVN Impact strength (J) |
(MPa) |
(MPa) |
(L= 5d)% |
at minus 20 C (Joules) |
620 | 550 | 24 |
80 |
CURRENT AND PACKING DATA:
STANDARD SIZE : 1.2 mm & 1.6 mm
QUANTITY : 15.0 kgs wire, layer wound in a plastic spool that conforms to DIN-8559 SD-300.
WELDING PARAMETER: DC(+)
Diameter |
Flat |
|
Volt, V |
Current, A |
|
1.2 mm |
27-32 |
300-360 |
1.6 mm |
25-30 |
340-420 |
SHIELDING GAS
Argon/ 1-5% O2
WELDING POSITION
H,F,VU,OH
Wire Material | SS |
Thickness | 1.2 mm |
Brand | D&H Secheron |
Usage/Application | Autotherme 308L Si is a solid wire for GMAW process, available in bright finish, gives smooth flow. |
I Deal In | New Only |
Quantity Per Roll | 12.5 kg |
Autotherme 308L Si is a solid wire for GMAW process, available in bright finish, gives smooth flow, stable arc and spatter free under optimum welding conditions. It gives radiographic quality welds. Wire contains low carbon 20Cr - 10Ni – Si, silicon improve the usability of the filler wire. The weld metal exhibits excellent resistance to Intergranular Corrosion. It is ideally suited for welding of stainless steels of similar composition like 304L and equivalents, for overlays, surfacing, and repairing castings of similar materials.
ApprovalsCHEMICAL COMPOSITION OF ALL WELD METAL (%)
Element |
C | Mn | Si | S | P | Cr | Ni |
Percent |
0.022 | 1.20 | 0.90 | 0.015 | 0.018 | 20.00 | 10.0 |
TYPICAL MECHANICAL PROPERTIES OF ALL WELD METAL
UTS | Elongation |
(MPa) |
(L= 4d)% |
540 | 38.0 |
Argon
CURRENT CONDITIONSDCEP
WELDING POSITIONSH, F, VU, OH
PACKINGSTANDARD SIZE: Diameter 0.8 mm, 1.2 mm & 1.6 mm
QUANTITY: 12.5 kgs wire, layer wound in a plastic spool that conforms to DIN 8559 SD-300.
Wire Material | MS |
Thickness | 1.2 mm |
Brand | D&H SECHERON |
Usage/Application | Autotherme Cr-Mo 5 is a copper-coated solid wire for GMAW, available in bright finish. |
I Deal In | New Only |
Quantity Per Roll | 15 kg |
Autotherme Cr-Mo 5 is a copper-coated solid wire for GMAW, available in bright finish. The wire gives stable arc, smooth welding performances and deposits radiographic quality welds. It is suitable for welding 5Cr 0.5Mo steel. The weld metal possesses good high temperature properties. The weld metal possesses excellent creep property up to 550 C. Especially suitable for welding of pipes and tubes of matching composition in Power plants, Refineries, Petrochemicals, Fertilizer plants, etc. Suitable for welding of ASTM steels: Grade F5/ F5a & F21 of SA-182, Grade T4, T22 of SA-199, Grade T22 of SA-213, Grade C5 of SA-217, Grade P22 of SA-335, Grade F5 & F21 (class 1&3) of SA-336, Grade FP5, FP21 of SA-369, Grade 5, 21 & 21L of SA-387, Grade CP5, CP21 of SA-426, Class 4, 4a of E types of SA-542, etc.
ApprovalsCETYPICAL CHEMICAL COMPOSITION OF SOLID WIRE
Element |
C | Mn | Si | S | P | Cr | Mo | Cu |
Percent |
0.06 | 0.50 | 0.40 | 0.010 | 0.012 | 5.20 | 0.55 | 0.10 |
TYPICAL MECHANICAL PROPERTIES OF ALL WELD METAL
(PWHT: 745°C FOR 1 HR)
UTS | Ys | Elongation |
(MPa) |
(MPa) |
(L= 5d)% |
600 | 520 | 25 |
STANDARD SIZE : 1.2 mm & 1.6 mm.
QUANTITY : 15.0 kg wire, layer wound in a plastic spool that conforms to DIN-8559 SD-300
WELDING PARAMETER : DC(+)
Diameter |
Flat |
|
Volt, V |
Current, A |
|
1.20 mm |
27-32 |
300-360 |
1.60 mm |
25-30 |
340-420 |
SHIELDING GAS
Argon/ 1.5% O2
WELDING POSITIONH, F, VU, OH
Wire Material | MS |
Thickness | 1.2 mm |
Brand | D&H Secheron |
Quantity Per Roll | 15 kg |
Autotherme Cr-Mo 9 is a copper-coated solid wire for GMAW, available in bright finish. The wire gives stable arc, smooth welding performances and deposits radiographic quality welds. It is designed for creep resistant steels. It is used for welding base metal of similar compositions, usually in the form of pipe or tubing. Typical applications include welding of A387 Grade 9 plate, A335 P9 pipe, A213 T9 tubes, etc.
ApprovalsCECHEMICAL COMPOSITION OF SOLID WIRE, WT. %:
Element |
C | Mn | Si | S | P | Cr | Mo | Cu |
Percent |
0.08 | 0.60 | 0.30 | 0.020 | 0.020 | 9.00 | 1.00 | 0.10 |
MECHANICAL PROPERTIES OF ALL WELD METAL
UTS | Ys | Elongation |
(MPa) |
(MPa) |
(L= 5d)% |
570 | 500 | 18 |
CURRENT AND PACKING DATA:
STANDARD SIZE : 1.2 mm & 1.6 mm
QUANTITY : 15.0 kgs wire, random/ layer wound in a plastic spool that conforms to DIN-8559 SD-300.
WELDING PARAMETER: DC(+)
Diameter |
Flat |
|
Volt, V |
Current, A |
|
1.2 mm |
27-32 |
300-390 |
1.6 mm |
25-30 |
340-420 |
SHIELDING GAS
Argon/ 1-5% O2
WELDING POSITION
H,F,VU,OH
Wire Material | MS |
Thickness | 1.2 mm |
Brand | D&H Secheron |
Quantity Per Roll | 15 kg |
Autotherme Cr-Mo 2 is a copper-coated solid wire for GMAW, available in bright finish. The wire gives stable arc, smooth welding performances and deposits radiographic quality welds. It is suitable for welding 2.25Cr - 1Mo steel. The weld metal possesses good high temperature properties. It deposits notch free weld deposit with excellent mechanical properties. Especially suitable for welding of pipes and tubes of matching composition in Power plants, Refineries, Petrochemicals, Fertilizer plants, etc. Suitable for welding of ASTM steels: Grade F22 (class 1 & 3) of SA-182 and SA-336, Grade T4, T22 of SA-199, Grade T22 of SA- 213, Grade WC9 of SA-217, Grade P22 of SA-335, Grade FP22 of SA-369, Grade 22, 22L of SA-387, Grade CP22 of SA-426, Grade 22 of SA-541, Class 1 of A, B types of SA-542, etc.
ApprovalsCIB-MPCECHEMICAL COMPOSITION OF SOLID WIRE, WT. %:
Element |
C | Mn | Si | S | P | Cr | Mo | Cu |
Percent |
0.09 | 0.50 | 0.55 | 0.010 | 0.012 | 2.50 | 1.10 | 0.10 |
MECHANICAL PROPERTIES OF ALL WELD METAL
UTS | Ys | Elongation |
(MPa) |
(MPa) |
(L= 5d)% |
680 | 600 | 19 |
STANDARD SIZE : 1.2 mm & 1.6 mm.
QUANTITY : 15.0 kg wire, layer wound in a plastic spool that
WELDING PARAMETER : DC(+)
Diameter |
Flat |
|
Volt, V |
Current, A |
|
1.20 mm |
27-32 |
300-360 |
1.60 mm |
25-30 |
340-420 |
SHIELDING GAS
Argon/ 1-5% O2
WELDING POSITIONH, F, VU, OH